HIGH MANGANESE STEEL PLATE

WARRIORS ACRONI, X12, 11- 14 % MANGANESE PLATE WARRIORS ACRONI, X12, 11- 14 % Manganese is a true Hadfield Austenitic Manganese steel for resistance to severe impact and abrasive wear. It is work hardening steel. WORK HARDENING refers to the fact that the steel becomes harder and harder the more it is impacted or compressed.

Awesome Image
Material GradeHigh Manganese Steel Plate
TypePLATE
Thickness>5 mm
BrandINDIAN
Size1250MMX2500MM/5000MM
MaterialHigh Manganese Steel Plate
Usage/ApplicationShot Blast Equipment Liners - Abrasive,Non-Magnetic Applications - RR Bolster Plates
ShapePLATE
Surface FinishingBRIGHT
StandardINDIAN

CHEMICAL COMPOSITION :


Typical Mechanical Properties


Hardness (As Delivered)

250 BHN

Tensile Strength

1, 32,000 PSI Min

Yield Strength

90,000 PSI Min

After work Hardening

550 BHN

The “Hadfield” grade has an original hardness of approximately 220 Brinell. With continued impact and /or compression it will surface harden to over 550 Brinell. It should be noted that only the outer skin surface hardens. The under layer remains highly ductile and tough. As the surface wears, it continually renews itself becoming harder and harder.

Manganese steel is austenitic steel which means it is non-magnetic. This property makes it useful in many applications such as bottom plates for lifting magnets – separator drum shells for magnetic materials – wear shoes on electric brakes etc.


ADVANTAGES :


Resistance to high abrasion and severe impact

Capacity of cold work hardening hardness to 550 BHN

To increase hardness from 200BHN (in as delivered plate) up to an in-service hardness of at least 600BHN

Have non-magnetic properties.

Provide Maximum Wear Life.

Exceptionally high toughness & ductility

Easy gas cutting & good weld ability


APPLICATION :


Shot Blast machines & Cabinets

Wheelabrator

Dust Collector

Shake out dates

Sintering Seal Bars

Screens

Crusher Liners

Grader Blades

Elevator Buckets

Baffle Plates

Stone Chutes

Bucket Liners

Crusher Jaws

Hammers

Chain Wear Bars

Grizzly Bars


MANGANESE ADVANTAGES

WORK HARDENING refers to the fact that the steel becomes harder and harder the more it is impacted or compressed

The “Hadfield” grade has an original hardness of approximately 220 BRINELL. With continued impact and /or compression it will surface harden to over 550 BRINELL. It should be noted that only the outer skin surface hardens. The under layer remains highly ductile and tough. As the surface wears, it continually renews itself becoming harder and harder.

Manganese steel is austenitic steel which means it is non-magnetic. This property makes it useful in many applications such as bottom plates for lifting magnets – separator drum shells for magnetic materials – wear shoes on electric brakes etc.

FORM OF SUPPLY :


THICKNESS RANGE:  0.25 MM up to 20.00 MM range as per following divisions and          thickness tolerance.


WIDTH RANGE: 5.00 MM up to 1250 MM however we can slit as per customers       requirement.


EDGE CONDITION: Mill Edge, Sheared Edge


COIL FORM: Material can be supplied in coil form


SHEET FORM: Material can be supplied in coil form


ADDITIONAL INFORMATION :


Production Capacity : 10MT

Delivery Time : SAME DAY

Packaging Details : AS PER CUSTOMER REQUIREMENT

FORM OF SUPPLY


THICKNESS RANGE: 5 MM up to 100 MM range as per following divisions and thickness       tolerance.

WIDTH RANGE: 1000 MM up to 2000 MM however we can slit as per customers       requirement.


EDGE CONDITION: Mill Edge, Sheared Edge


COIL FORM:   Material can be supplied in sheet form as well


SHEET FORM: Material can be supplied in sheet form as well


Material can be supplied in sheet form as well